Bond strength comparison among 10-MDP-containing and non-10-MDP-Containing adhesives in different degrees of dental fluorosis / Comparación de fuerza de unión entre adhesivos que contienen y no contienen 10-MDP en diferentes grados de fluorosis dental

Dental fluorosis can cause changes in the enamel surface, conditioning its functionality and esthetics. The application of dental adhesives is a treatment option; however, their use on fluorotic teeth can result in limitations. The aim of this study was to compare the shear bond strength of two different adhesives, one with 10-MDP and one without 10-MDP, in different degrees of dental fluorosis.This is an in vitro study on dental enamel samples, a total of 180 samples with the inclusion criteria were treated, randomly divided into two groups of 90, according to the type of dental adhesive, where each group was again divided into three groups of 30 samples, representing different degrees of dental fluorosis according to the Thylstrup-Fejerskov index (Group I: TF1 and TF2; Group II: TF3; Group III: TF4). Normality tests, two-factor ANOVA, and post-hoc tests were used to determine differences between the groups, with a significance level of 95%. As results, a statistically significant difference was shown between the use of dental adhesive with 10-MDP and the three groups of dental fluorosis (p=0.011), in addition, a Tukey post-hoc test on the groups treated with 10-MDP adhesive revealed a statistically significant difference between group I versus group II, and group I versus group III, (p=<0.05). It is concluded that the use of adhesive systems with 10-MDP presents a better shear bond strength on enamel with dental fluorosis grades I and II in the Thylstrup-Fejerskov index.

La fluorosis dental puede ocasionar cambios en la superficie del esmalte, condicionando su funcionalidad y estética, la aplicación de adhesivos dentales es una opción de tratamiento, sin embargo, su uso en dientes fluoroticos puede resultar en limitaciones. El objetivo de este estudio consistió en comparar la fuerza de adhesión a la cizalladura de dos diferentes adhesivos, uno con 10-MDP y otro sin 10-MDP, en diferentes grados de fluorosis dental. Se trata de un estudio in vitro en muestras de esmalte dental, un total de 180 muestras con los criterios de inclusión fueron tratadas, aleatoriamente divididas en dos grupos de 90, de acuerdo al tipo de adhesivo dental, donde cada grupo fue dividido nuevamente en tres grupos de 30 muestras, representando diferentes grados de fluorosis dental según el índice de Thylstrup- Fejerskov (Grupo I: TF1 y TF2; Grupo II: TF3; Grupo III: TF4). Para determinar diferencias entre los grupos se utilizaron pruebas de normalidad, ANOVA de dos factores, y pruebas post-hoc, con un nivel de significancia de 95%. Como resultados, se mostró una diferencia estadísticamente significativa entre el uso de adhesivo dental con 10- MDP y los tres grupos de fluorosis dental (p=0.011), además, una prueba post hoc de Tukey sobre los grupos tratados con adhesivo 10-MDP revelaron una diferencia estadísticamente significativa entre el grupo I frente al grupo II, y el grupo I frente al grupo III, (p=<0.05) Se concluye que el uso de sistemas adhesivos con 10-MDP presentan una mejor resistencia de adhesión al cizallamiento en esmalte con grados de fluorosis dental I y II en el índice de Thylstrup-Fejerskov

Bond strength of composite resin/universal adhesive to dentin submitted to radiotherapy / Fuerza de unión de resina compuesta/adhesivo universal a dentina sometida a radioterapia

Aim: To evaluate the bond strength of a universal adhesive system to dentin submitted to radiotherapy. Materials and Methods: Sixty extracted human teeth were divided into two groups (n = 30): without radiotherapy (control); with radiotherapy, according to the adhesive protocol (n=15): ER-etch-and-rinse (acid + Single Bond Uni-versal); SE-self-etch (Single Bond Universal). The analyzes were shear bond strength (SBS) (n=10), failure pattern (n=10) and scanning electron microscopy (n=5). Data was analyzed by a two-way ANOVA (α =0.05). Results: The radiotherapy decreased SBS of the restorative material to dentin (p<0.0001). The ER protocol provided lower bond strength values (p<0.001). The predominant type of fracture without radiotherapy was mixed (SE), cohesive to the material (ER). Both protocols presented adhesive failures with radiotherapy. Teeth had a hybrid layer and long resin tags (without radiotherapy) and few tags (with radiotherapy). Conclusions: The SE adhesive mode favors the shear bond strength of resin to dentin in teeth submitted to radiotherapy.

Objetivo: Evaluar la fuerza de adhesión de un sistema adhesivo universal a la dentina sometida a radioterapia. Materiales y Métodos: Sesenta dientes humanos extraídos se dividieron en dos grupos (n = 30): sin radioterapia (control); con radioterapia, según protocolo adhesivo (n=15): ER-grabado y enjuague (ácido + Single Bond Universal); autograbado SE (Single Bond Universal). Los análisis ejecutados fueron resistencia al cizallamiento (SBS) (n=10), patrón de falla (n=10) y microscopía electrónica de barrido (n=5). Los datos se sometieron al test de ANOVA de dos vías (α =0,05). Resultados: La radioterapia disminuyó la SBS del material restaurador a la dentina (p<0,0001). El protocolo ER proporcionó valores de fuerza de unión más bajos (p<0,001). El tipo de fractura predominante sin radioterapia fue mixta (SE), cohesiva al material (ER). Ambos protocolos presentaron fallas adhesivas con radioterapia. Los dientes tenían una capa híbrida y colas de resina largas (sin radioterapia) o pocas colas de resina (con radioterapia). Conclusión: El modo adhesivo SE favorece la resistencia al corte de la resina a la dentina en dientes sometidos a radioterapia.

Resistencia de unión al cizallamiento de diferentes agentes de fijación a aleaciones metálicas odontológicas / Shear bond strength of different bonding agents to dental metal alloys

Introducción: La fijación de las restauraciones indirectas es uno de los pasos más importantes, para conseguir una adecuada retención y sellado de la interfase entre el material restaurador y el diente. Objetivo: Evaluar la resistencia de unión al cizallamiento de diferentes agentes de fijación a dos aleaciones metálicas utilizadas en odontología. Métodos: Estudio experimental in vitro. Cien especímenes de aleaciones de metales base, 50 de níquel-cromo y 50 de níquel-cromo-titanio fueron preparados y divididos de manera aleatoria en 5 grupos. Esta división se realizó acorde con el agente de fijación utilizado: sistema autograbante de dos pasos (Clearfil SE Bond; CSB), sistema adhesivo universal (Single Bond Universal; SBU), cemento resinoso autoadhesivo (Maxcem Elite; ME), ionómero de vidrio (IV) y fosfato de zinc (ZnPO). Posteriormente a la aplicación de cada agente de fijación, los especímenes tratados fueron almacenados en agua destilada por 24 h a 37 ºC y sometidos a un ensayo de resistencia de unión al cizallamiento. Resultados: La resistencia de unión al cizallamiento fue influenciada significativamente por el tipo de agente de fijación (p = 0,002) y el tipo de aleación utilizada (p < 0,001). La resistencia de unión al cizallamiento fue mayor, al utilizar el sistema Clearfil SE Bond, seguida de Single Bond Universal; las diferencias entre Maxcem Elite y el Fosfato de zinc no fueron significativas. Finalmente, el IV no mostró adhesión a ninguna de las aleaciones metálicas utilizadas. Conclusiones: El uso de Clearfil SE Bond aumentó la resistencia de unión de los cementos resinosos a las aleaciones metálicas(AU)

Introduction: The bonding of indirect restorations is one of the most important steps, in order to achieve adequate retention and sealing of the interface between the restorative material and the tooth. Objective: To evaluate the shear bond strength of different bonding agents to two metal alloys used in dentistry. Methods: In vitro experimental study. One hundred specimens of base metal alloys, 50 nickel-chromium and 50 nickel-chromium-titanium were prepared and randomly divided into 5 groups. This division was made according to the bonding agent used: two-step self-etching system (Clearfil SE Bond; CSB), universal adhesive system (Single Bond Universal; SBU), self-adhesive resin cement (Maxcem Elite; ME), glass ionomer (IV) and zinc phosphate (ZnPO). After the application of each bonding agent, the treated specimens were stored in distilled water for 24 hr at 37 ºC and subjected to a shear bond strength test. Results: Shear bond strength was significantly influenced by the type of bonding agent (p = 0.002) and the type of alloy used (p < 0.001). Shear bond strength was highest when using the Clearfil SE Bond system, followed by Single Bond Universal; the differences between Maxcem Elite and Zinc Phosphate were not significant. Finally, IV did not show adhesion to any of the metal alloys used. Conclusions: The use of Clearfil SE Bond increased the bond strength of resinous cements to metallic alloys(AU)

Influence of etching Mode and composite type on bond strength to biodentine using a ''No-Wait'' universal adhesive / Influencia del modo de grabado y del tipo de resina en la resistencia adhesiva al Biodentine utilizando un adhesivo universal tipo "no-wait"

Abstract: The purpose of this study was to compare the shear bond strength (SBS) of four resin-based composite materials to a silicate-based cement using a ''no-wait'' universal bond with self-etch (SE) and etch-and-rinse (ER) modes. Acrylic blocks (n=80, 2mm depth, 5mm diameter central hole) were prepared. The holes were filled with BiodentineTM (BD) and divided into 4 main groups (n=20) according to the composite resin type used: Group FZ250: FiltekTM Z250 Universal Restorative (microhybrid), Group SDR: SDR Plus U Bulk Fill Flowable (low-viscosity bulk-fill), Group FBP: FiltekTM Bulk Fill Posterior (high-viscosity bulk-fill), Group EF: EsFlow™ Universal Flowable Composite (nanohybrid). A 'no-wait' universal bond (Clearfil Universal Bond Quick) was used for bonding application. Then each group was divided into 2 subgroups according to the etching mode applied (ER and SE). SBSs were measured and stereomicroscope was used to identify the failure modes. Selected samples of fracture surfaces were imaged by SEM. Tukey's post-hoc and One-way ANOVA tests were used to analyze data. There were statistically significant differences among the composite groups (p 0.05). The SBS of BD to the resin composites depends on the composite type but application of the 'no-wait' universal bond in different etching modes is regardless of the SBS of BD to resin composites.

Resumen El objetivo de este estudio fue comparar la resistencia de adhesión al cizallamiento (SBS) de cuatro resinas con un cemento a base de silicato utilizando una adhesivo universal "no-wait" de autograbado (SE) y grabado y lavado (ER). Se prepararon bloques acrílicos (n=80, de 2mm de profundidad y un agujero central de 5mm de diámetro). Los agujeros se rellenaron con BiodentineTM (BD) y se dividieron en 4 grupos principales (n=20) según el tipo de resina compuesta utilizada: Grupo FZ250: FiltekTM Z250 Universal Restorative (microhíbrido), Grupo SDR: SDR Plus U Bulk Fill Flowable (bulk-fill de baja viscosidad), Grupo FBP: FiltekTM Bulk Fill Posterior (bulk-fill de alta viscosidad), Grupo EF: EsFlow™ Universal Flowable Composite (nanohíbrido). Para la aplicación de la adhesión se utilizó un adhesivo universal "no-wait" (Clearfil Universal Bond Quick). A continuación, cada grupo se dividió en 2 subgrupos según el modo de grabado aplicado (ER y SE). Se midieron los SBS y se utilizó el estereomicroscopio para identificar los modos de fallo. Las muestras seleccionadas de las superficies de fractura se analizaron mediante SEM. Se utilizaron las pruebas post-hoc de Tukey y ANOVA de una vía para analizar los datos. Hubo diferencias estadísticamente significativas entre los grupos de composites (p0,05). La SBS de la BD a los composites de resina depende del tipo de composite, pero la aplicación de la unión universal "no-wait" en los diferentes modos de grabado es independiente de la SBS de la BD a los composites de resina.

How does radiotherapy affect the adhesion of universal adhesive to enamel and dentin? A qualitative and quantitative analysis? / Efecto de la radioterapia a la adhesión del adhesivo universal al esmalte y dentina? Un análisis cualitativo y cuantitativo?

Abstract This study investigated the shear bond strength (SBS) of a universal adhesive to enamel/dentin; 1) that had undergone radiotherapy (RT) and 2) that were readily restored and had undergone RT. Enamel and dentin surfaces were obtained from 90 intact human molars. They were randomly divided into six groups according to the presence and timing of irradiation (RT0:no radiotherapy/control, RT1:RT before restoration, RT2:RT after restoration groups) and adhesive application modes (etch&rinse/ER, self-etch/SE)(n=15). A universal adhesive and resin composites were applied. The radiotherapy protocol was conducted with 60 Gy. The SBS test was subjected (1mm/min) and failure type analysis was performed. The resin-enamel/dentin interfaces were examined. Data were statistically analyzed. For enamel and dentin, the presence and timing of irradiation did not significantly influence the SBS values (p>0.05). For enamel, significantly higher SBS values were obtained using etch&rinse mode than self-etch mode (p<0.05). The predominant failure was mixed type. Loss of enamel prisms and obliterated irregular dentinal tubules were found for the radiotherapy-treated specimens. Resin tags were clearer in the irradiated enamel treated with ER than SE. Irradiation with different timings did not influence the bond strength to enamel and dentin, negatively. Irrespective of radiotherapy, the etch&rinse mode caused higher bond strength to enamel than self-etch mode.

Resumen Este estudio investigó la fuerza de unión al cizallamiento (SBS) de un adhesivo universal al esmalte/dentina en piezas que se habían sometido a radioterapia (RT). Se obtuvieron superficies de esmalte y dentina de 90 molares humanos intactos. Se dividieron aleatoriamente en seis grupos según la presencia y el momento de la irradiación (RT0: sin radioterapia/control, RT1: RT antes de la restauración, RT2: RT después de la restauración considerando los modos de aplicación del adhesivo (n=15). Se aplicó un adhesivo universal y resinas compuestas. El protocolo de radioterapia se realizó con 60 Gy. Se sometió a la prueba adhesiva (1mm/min) y se realizó análisis del tipo de falla. Se examinaron las interfases resina-esmalte/dentina. Los datos fueron analizados estadísticamente. Para el esmalte y la dentina, la presencia y el momento de la irradiación no influyeron significativamente en los valores adhesivos (p>0,05). Para el esmalte, se obtuvieron valores adhesivos significativamente más altos utilizando el modo de grabado y enjuague que el modo de autograbado (p<0,05). La falla predominante fue de tipo mixto. Se encontró pérdida de prismas de esmalte y túbulos dentinarios irregulares obliterados en las muestras tratadas con radioterapia. La irradiación con diferentes tiempos no influyó negativamente en la fuerza de unión al esmalte ni a la dentina. Independientemente de la radioterapia, el modo de grabado ácido y enjuague provocó una mayor fuerza de adhesión al esmalte que el modo de autograbado.

Uso de adhesivo universal con pregrabado y autograbado en tejidos duros del diente / Use of universal adhesive with pre-etch and self etch strategies on hard tooth tissues

RESUMEN Introducción: Buscando satisfacer la demanda con procedimientos adhesivos más rápidos, menos sensibles a la técnica y facilidad de uso, se han desarrollado los adhesivos universales, que brindan al profesional la opción de seleccionar la estrategia de adhesión con diferentes modos de grabado, ya sea con grabado y enjuague, autograbado o grabado selectivo. Debido a la poca información existente, se han generado dudas sobre el rendimiento, propiedades y la aplicación de una técnica adhesiva adecuada sobre los tejidos dentales. Objetivo: Determinar el nivel de adhesión con el uso de adhesivos universales en modo de grabado y enjuague y autograbado. Métodos: Se realizó una revisión de la literatura, a través de la búsqueda electrónica en las bases de datos: SciELO, Scopus, PubMed, Springer y EBSCO. Inicialmente se seleccionaron por título y resumen, artículos duplicados se consideraron solo una vez, se incluyeron artículos de acceso libre y pagos, escritos en idioma español e inglés, publicados desde el año 2015, de los cuales 39 artículos fueron seleccionados para el estudio. Conclusiones: El uso de adhesivos universales sobre dentina presenta un nivel de adhesión mayor cuando se aplica en modo de autograbado. La aplicación activa del adhesivo universal en esmalte mejora la fuerza y resistencia de unión. El nivel de adhesión en el esmalte es mayor cuando se aplica en modo de grabado y enjuague. La resistencia inicial y por fatiga del adhesivo, no mejora con los tiempos prolongados del grabado ácido.

ABSTRACT Introduction: universal adhesives have been developed to satisfy the demand with faster adhesive procedures, less sensitive to the technique and ease of use, which offer the professional the option of selecting the adhesion strategy with different etching modes, either with etch-and-rinse, self-etch or selective etching ones. Doubts have been generated about the performance, properties and application of an adequate adhesive technique on dental tissues due to the little existing information. Objective: to determine the level of adhesion with the use of universal adhesives in etch-and-rinse and self-etch modes Methods: an electronic search of the literature was carried out in SciELO, Scopus, PubMed, Springer and EBSCO databases. Initially, articles were selected by title and abstract, duplicate ones were considered only once, free and paid access articles, written in Spanish and English and published since 2015 were included; 39 of them were selected for the study. Conclusions: the use of universal adhesives on dentin presents a higher level of adhesion when applied in self-etch mode. The active application of the universal adhesive improves the enamel bond strength. The level of adhesion on the enamel is higher when applied in etch-and-rinse. The initial fatigue resistance of the adhesive does not improve with prolonged acid etching times.

Endocorona, un enfoque diferente en rehabilitación oral

RESUMEN Introducción: Con el avance de la tecnología adhesiva, nuevas técnicas y materiales restauradores están siendo utilizados para el tratamiento de dientes endodonciados, por ello, las endocoronas son una alternativa clínica para su tratamiento. La ventaja de esta restauración es que tiene mejores características macro retentivas, requiere menor tiempo clínico y de laboratorio. Objetivo: Proporcionar información bibliográfica actual sobre esta nueva alternativa para aplicar una nueva guía en rehabilitación oral con el uso de la endocorona mediante una revisión de la literatura. Método: Se realizó una revisión bibliográfica detallada, con la consideración de artículos originales o casos clínicos que incluían información relacionada a las restauraciones de tipo endocorona. La búsqueda se efectuó en las bases de datos PubMed, SciELO, Science Direct, Elsevier y Google Académico. Resultados: Las restauraciones de tipo endocorona son un monobloque único que devuelve la anatomía completa de la corona dental, la cual aprovecha la cámara pulpar para así lograr una mayor adhesión y macro retención mecánica. Este enfoque restaurador proporciona una función adecuada y estética, así como la integridad biomecánica de las estructuras no vitales. Conclusiones: Actualmente en la Odontología moderna se emplea el término de mínima intervención, conservando en su mayor cantidad posible el tejido dental de manera que los dientes tengan mayor funcionalidad, por ello las endocoronas son una opción segura y con buen pronóstico a largo plazo en rehabilitación oral para tratar piezas endodonciadas, debido a que es un procedimiento técnicamente más conservador, estético, sencillo y de menor costo.

ABSTRACT Introduction: With the advancement of adhesive technology, new techniques and restorative materials are being used for the treatment of root canals; therefore endocrowns are a clinical alternative for their treatment. The advantage of this restoration is that it has better macro retentive characteristics, requires less clinical and laboratory time. Objective: To provide current bibliographic information on this new alternative to apply a new guide in oral rehabilitation with the use of endocrown through a literature review. Method: A detailed bibliographic review was carried out, with the consideration of original articles or clinical cases that included information related to endocrown-type restorations. The search was carried out in the databases PubMed, SciELO, Science Direct, Elsevier and Google Scholar. Results: Endocrown restorations are a single monoblock that rebuilds the complete anatomy of the dental crown, which takes advantage of the pulp chamber to achieve greater adhesion and macro mechanical retention. This restorative approach provides adequate function and aesthetics, as well as the biomechanical integrity of non-vital structures. Conclusions: The term minimal intervention is currently very used in modern dentistry, preserving the dental tissue as much as possible so that the teeth have greater functionality. Endocrowns are a safe option with a good long-term prognosis in oral rehabilitation to treat root canals, because it is a technically more conservative, aesthetic, simple and lower-cost procedure.

RESUMO Introdução: Com o avanço da tecnologia adesiva, novas técnicas e materiais restauradores estão sendo utilizados para o tratamento de dentes endodônticos, portanto os endocrowns são uma alternativa clínica para seu tratamento. A vantagem dessa restauração é que ela apresenta melhores características macro retentivas, requer menos tempo clínico e laboratorial. Objetivo: Fornecer informações bibliográficas atuais sobre esta nova alternativa de aplicação de um novo guia na reabilitação oral com o uso de endocrown por meio de uma revisão da literatura. Método: Foi realizada uma revisão bibliográfica detalhada, considerando artigos originais ou casos clínicos que incluíam informações relacionadas a restaurações do tipo endocrown. A busca foi realizada nas bases de dados PubMed, SciELO, Science Direct, Elsevier e Google Scholar. Resultados: As restaurações do tipo endocrown são um único monobloco que devolve a anatomia completa da coroa dentária, que aproveita a câmara pulpar para obter maior adesão e retenção macromecânica. Esta abordagem restauradora fornece função e estética adequadas, bem como a integridade biomecânica de estruturas não vitais. Conclusões: Atualmente na odontologia moderna é utilizado o termo de intervenção mínima, preservando-se o tecido dentário o máximo possível para que os dentes tenham maior funcionalidade, portanto endocrowns são uma opção segura e com bom prognóstico em longo prazo na reabilitação oral para tratamento da endodontia dentes, por ser um procedimento tecnicamente mais conservador, estético, simples e de menor custo.

Contaminación de la dentina con diferentes técnicas de secado / Contamination of dentin with different drying techniques

El secado es uno de los factores clave para lograr una adhesión micromecánica exitosa en la dentina con los sistemas adhesivos de grabado independiente. El objetivo de este trabajo fue comparar los residuos remanentes luego de cuatro procedimientos diferentes de secado en preparaciones ex vivo en dentina. Se utilizaron cinco terceros molares ex-vivo, en cada uno de los cuales se realizó una preparación dentinaria en piso y paredes con al menos un socavado. Las unidades experimentales fueron almacenadas en solución fisiológica durante 7 días. Las distintas técnicas de secado (G1- G8) se aplicaron, luego de que las preparaciones fueron tratadas con gel de ácido fosfórico al 37% (Blue Gel etch Megadental) durante 15s y lavadas con jeringa y agua a presión durante 15s (Técnica de Grabado Ácido o TGA), de la siguiente manera: algodón común (Condesa) (G1), papel tisú (Achiss) cortado a mano (G2) y con tijera (G3), esponja (Sharpys) (G4), papel tisú (Simplicity) cortado a mano (G5)(AU)

Recuento de Streptococcus mutans sobre restauraciones realizadas con adhesivo con y sin carga de nanopartículas de óxido de zinc y cobre / Streptococcus mutans count on restorations made with adhesive with and without loading zinc and copper oxide nanoparticles

Objetivo: Determinar las propiedades antimicrobianas de la incorporación de nanopartículas de óxido de zinc y cobre en un adhesivo de grabado y lavado total sobre Streptococcus mutans en pacientes con restauraciones de resina compuesta confeccionadas con adhesivo cargado. Métodos: Estudio experimental, randomizado, la muestra estuvo conformada por 25 pacientes, de ambos sexos, pertenecientes al posgrado de Ortodoncia de la Facultad de Odontología de la Universidad de Chile, en los cuales se confirmó presencia de Streptococcus mutans en saliva. Se confeccionaron restauraciones de resina compuesta oclusales, en premolares superiores con indicación de exodoncia por el tratamiento de ortodoncia, con adhesivo cargado (cuya composición fue 5/0,2 por ciento ZnO y Cu, respectivamente) y control (sin presencia de nanopartículas en su composición), según el listado de aleatorización. Se tomaron muestras microbiológicas en tres tiempos con la técnica de la cubeta (antes, 1 semana y 4 semanas posterior a la confección de las restauraciones). Se obtuvieron, aislaron e identificaron colonias de Streptococcus mutans a partir de las muestras obtenidas. Se usó el test de Mann-Whitney mediante el paquete estadístico SPSS v.21 Resultados: El promedio del recuento de UFC de Streptococcus mutans en el grupo experimental fue mayor posterior a la confección de las restauraciones de resina compuesta. Los resultados de la identificación molecular por PCR demuestran la presencia de Streptococcus mutans en 20 de 25 muestras. Conclusiones: No existen diferencias en el recuento de Streptococcus mutans antes y después de la aplicación del adhesivo sobre las restauraciones de resina compuesta(AU)

Objective: To determine the antimicrobial properties of the incorporation of zinc and copper oxide nanoparticles in an etching and total wash adhesive on Streptococcus mutans in patients with composite resin restorations made with loaded adhesive. Methods: Experimental and randomized trial, the sample were 25 patients, of both sexes, belonging to the FOUCH Orthodontic postgraduate program, in whom the presence of Streptococcus mutans in saliva was confirmed. Occlusal composite resin restorations were made in upper premolars with indication of extraction by orthodontic treatment, with loaded adhesive (whose composition is 5 / 0.2% ZnO and Cu respectively) and control (without the presence of nanoparticles in their composition), according to the scrambling listing. Microbiological samples were taken in three stages with the cuvette technique (before, 1 week and 4 weeks after the restoration was made). Colonies of Streptococcus mutans were obtained, isolated and identified from the samples obtained. The statistical analysis used the SPSS v.21 software, the data was analyzed by Mann Whitney test Results: The average CFU count of Streptococcus mutans in the experimental group (adhesive modified with zinc oxide and copper nanoparticles) was higher after the fabrication of composite resin restorations. The results of molecular identification by PCR demonstrate the presence of Streptococcus mutans in 20 of 25 samples. Conclusions: There are no differences in the count of Streptococcus mutans before and after the application of the adhesive on the composite resin restorations(AU)

Efecto antimicrobiano sobre Streptococcus mutans de sistema adhesivo con nanopartículas de óxido de zinc y cobre / Antimicrobial effect against Streptococcus mutans of an adhesive system with copper and zinc oxide nanoparticles

Objetivo: Determinar las propiedades antimicrobianas de la incorporación de nanopartículas de óxido de zinc y cobre en un adhesivo de grabado y lavado total sobre Streptococcus mutans en pacientes con restauraciones de resina compuesta confeccionadas con adhesivo cargado. Métodos: Este estudio clínico randomizado, participaron 25 pacientes, de ambos sexos, pertenecientes al posgrado de Ortodoncia de la Facultad de Odontología de la Universidad de Chile, en los cuales se confirmó presencia de Streptococcus mutans en saliva. Se confeccionaron restauraciones de resina compuesta oclusales, en premolares superiores con indicación de exodoncia por el tratamiento de ortodoncia, con adhesivo cargado (cuya composición es 5 / 0.2 por ciento ZnO y Cu respectivamente) y control (sin presencia de nanopartículas en su composición), según el listado de aleatorización. Se tomaron muestras microbiológicas en tres tiempos con la Técnica de la cubeta (antes, 1 semana y 4 semanas posterior a la confección de las restauraciones). Se obtuvieron, aislaron e identificaron colonias de Streptococcus mutans a partir de las muestras obtenidas. Los datos fueron analizados por el test de Mann Whittney. Resultados: El promedio del recuento de UFC (unidades formadoras de colonias) de Streptococcus mutans en el grupo experimental fue mayor posterior a la confección de las restauraciones de resina compuesta.Los resultados de la identificación molecular por PCR demuestran la presencia de Streptococcus mutans en 20 de 25 muestras. Conclusiones: No existen diferencias en el recuento de Streptococcus mutans antes y después de la aplicación del adhesivo sobre las restauraciones de resina compuesta(AU)

Objective: Determine the antimicrobial properties of the incorporation of copper and zinc oxide nanoparticles into a total rinse and etch adhesive against Streptococcus mutans in patients with composite resin restorations made with loaded adhesive. Methods: A randomized clinical study was conducted of 25 patients of both sexes from the orthodontics graduate course taught at the Dental School of the University of Chile, in whom the presence of Streptococcus mutans was confirmed in saliva. Occlusal composite resin restorations were performed in upper premolars with exodontia indicated as part of the orthodontic treatment, using loaded adhesive (composition 5 / 0.2 percent ZnO and Cu, respectively) and control (without nanoparticles in its composition), according to the randomization list. Microbiological samples were taken at three moments applying the tray technique (before, 1 week after and 4 weeks after the restorations). Streptococcus mutans were obtained, isolated and identified from the samples taken. Data analysis was based on the Mann-Whitney test. Results: Mean Streptococcus mutans CFU count in the experimental group was higher after the composite resin restorations were made. Results of PCR molecular identification show the presence of Streptococcus mutans in 20 of 25 samples. Conclusions: No differences were found in the Streptococcus mutans count before and after application of the adhesive over the composite resin restorations(AU)

Effect of 10% sodium ascorbate applied for different time periods on shear bond strength of composite to bleached enamel / Efecto del 10% de ascorbato de sodio aplicado durante diferentes períodos de tiempo sobre la resistencia al cizallamiento del material compuesto al esmalte blanqueado

Aims: Residual peroxide on the enamel surface and in the interprismatic spaces decreases the shear bond strength (SBS) of composite to bleached enamel. Evidence shows that 10% sodium ascorbate can efficiently neutralize the singlet oxygen generated by the bleaching agents. This study aimed to assess the effect of duration of application of sodium ascorbate on SBS of composite to bleached enamel. Materials and Methods: This in vitro experimental study was conducted on 30 sound human third molars, which were randomly divided into three groups (n=10). In group 1, the teeth were bleached for 45 minutes and were then subjected to immediate bonding and restoration with composite resin. In groups 2 and 3, the teeth were bleached, immersed in 10% sodium ascorbate solution for 5 (group 2) and 10 (group 3) minutes and were then bonded and restored with composite, and the SBS was then measured. Results: The highest SBS (14.02±8.6MPa) was noted in group 3 (immersion in 10% sodium ascorbate for 10 minutes before bonding). The lowest SBS was noted in group 1 (immediate bonding after bleaching) (p<0.05). The difference in SBS of groups 1 and 2 was not significant (p=0.4). Conclusion: Application of 10% sodium ascorbate for 10 minutes increases the SBS of composite to bleached enamel.

Objetivos: el peróxido residual en la superficie del esmalte dental y en los espacios interprismáticos disminuye la resistencia al cizallamiento (R AC) de la resina compuesta al esmalte dental blanqueado. La evidencia muestra que el 10% de ascorbato de sodio puede neutralizar eficientemente el oxígeno singlete generado por los agentes blanqueadores. Este estudio tuvo como objetivo evaluar el efecto de la duración de la aplicación de ascorbato de sodio en la R AC de la resina compuesta al esmalte dental blanqueado. Materiales y Metodos: Este estudio experimental in vitro se realizó en 30 terceros molares humanos sanos, que se dividieron aleatoriamente en tres grupos (n=10). En el grupo 1, los dientes se blanquearon durante 45 minutos y luego se sometieron a una unión y restauración inmediata con resina compuesta. En los grupos 2 y 3, los dientes se blanquearon, se sumergieron en una solución de ascorbato de sodio al 10% durante 5 (grupo 2) y 10 (grupo 3) minutos y luego se unieron y restauraron con resina compuesta; luego se midió la R AC. Resultados: La R AC más alta (14,02 ± 8,6 MPa) se observó en el grupo 3 (inmersión en ascorbato de sodio al 10% durante 10 minutos antes de la unión). El valor de R AC más bajo se observó en el grupo 1 (unión inmediata después del blanqueo) (p<0,05). La diferencia en R AC de los grupos 1 y 2 no fue significativa (p=0,40). Conclusión: la aplicación de ascorbato de sodio al 10% durante 10 minutos aumenta la R AC de la resina compuesta al esmalte dental blanqueado.

Efecto de la aplicación activa con aplicadores mejorados de un adhesivo universal / Effect of the active application of a universal adhesive with improved applicators

RESUMEN Introducción: La permeabilidad dentinaria es conocida como el paso de fluidos, iones, partículas, moléculas y bacterias a través de la dentina bajo ciertas condiciones. Objetivo: Determinar la influencia de la aplicación activa con un aplicador mejorado de un adhesivo dentinario sobre la conductancia hidráulica dentinaria humana, in vitro. Métodos: Estudio experimental in vitro en 40 terceros molares libres de caries, con indicación de exodoncia, provenientes de pacientes sanos entre 15 y 30 años, previo consentimiento informado. Posteriormente se limpiaron, desinfectaron y conservaron para ser incluidos en bloques de resina epóxica. Luego se realizaron cortes transversales y se obtuvieron discos dentinarios de 1,5 mm de espesor y 25 mm de diámetro. Se dividieron en dos grupos de 20 unidades cada uno, se sometieron a grabado con ácido ortofosfórico al 37 por ciento, y se lavaron y secaron. Sobre una balanza de precisión se les aplicó adhesivo dentinario fotopolimerizable, registrando la fuerza ejercida. En el grupo 1 se usó un microbrush en la aplicación y en el grupo 2 un aplicador mejorado diseñado especialmente. Posteriormente cada muestra fue sometida a una cámara de difusión para obtener la tasa de flujo y luego calcular la conductancia hidráulica, la cual otorga información acerca de la permeabilidad de la dentina. Resultados: los resultados obtenidos fueron levemente menores en el grupo 2, sin embargo, experimentaron una distribución normal. Conclusiones: no existen diferencias significativas, al ser analizados estadísticamente bajo diversas pruebas, en los valores de conductancia hidráulica. Tampoco se pudo establecer una relación inversa entre la fuerza de aplicación de un adhesivo en forma activa con un aplicador mejorado y la conductancia hidráulica, por lo cual no se aconseja el uso de dicho instrumento(AU)

ABSTRACT Introduction: Dentin permeability is defined as the passage of fluids, ions, particles, molecules and bacteria through the dentin under certain conditions. Objective: Determine the effect of the active application of a dentin adhesive with an improved applicator on human dentin hydraulic conductance in vitro. Methods: An in vitro experimental study was conducted of 40 caries-free third molars with an indication of exodontia from healthy patients aged 15-30 years, prior informed consent. The molars were cleaned, disinfected and preserved to be included in epoxy resin blocks. Cross-sectional cuts were then made to obtain dentin discs 1.5 mm thick and 25 mm in diameter. These were divided into two 20-unit groups, were subjected to etching with 37 percent orthophosphoric acid, and were washed and dried. On a precision scale photopolymerizable dentin adhesive was applied, recording the force exerted. Application was performed with a Microbrush applicator in Group 1 and with an improved dedicated applicator in Group 2. The samples were then placed in a diffusion chamber to determine flow rate and subsequently estimate hydraulic conductance, thus obtaining information about dentin permeability. Results: Results were slightly lower in Group 2, but they displayed normal distribution. Conclusions: Statistical analysis with various tests did not find any significant differences in hydraulic conductance values, nor could an inverse relation be established between the force of active application of an adhesive with an improved applicator and hydraulic conductance. Therefore, use of that instrument is not advised(AU)

Marginal filling and adhesive resistance of bulk fill resin applying 18% edta gel compared with 37% phosphoric acid gel in vitro dental conditioning / Sellado marginal y resistencia adhesiva de resina bulk fill aplicando gel de edta al 18% comparado con el gel de ácido fosfórico al 37% en el acondicionamiento dental in vitro

Objective. To evaluate the degree of marginal sealing and adhesive strength in Bulk-Fill resin by applying 18% EDTA gel compared to 37% phosphoric acid gel in dental conditioning. Materials and methods. The study was transversal, experimental comparative, and applied. The sample group consisted of 60 teeth with Class I cavities, which were later subjected to conditioning. This was carried out separately with phosphoric acid gel for 15 seconds, and 18% EDTA gel within two different time frames: 60 and 90 seconds. All samples were incubated at 37ºC for a period of 24 hours and thermocycled between 5 to 55ºC for 500 cycles. To assess microfiltration, they were immersed in methylene blue at 37ºC for 4 hours, and were later sectioned and observed through a stereomicroscope. In order to perform the traction, the conventional testing machine was used at a speed of 0.75mm/min until the screw with the resin detached. Results: Samples conditioned with 37% phosphoric acid showed a greater degree 1 microfiltration and a mean adhesive resistance of 7.97 MPa. The same number of microfiltration grades 1 and 2 was found when using EDTA gel for 60 seconds, with a mean tensile strength of 8.8 MPa. On the other hand, applying EDTA gel for 90 seconds showed mostly grade 1 microfiltrations, and to a lesser extent, grade 0 and 2, with a mean resistance of 9.2 MPa. Conclusion: There are no statistically significant differences regarding adhesive strength between the two gels; however, better marginal filling was observed when samples were conditioned with 18% EDTA gel for 90 seconds.

Objetivo. Evaluar el grado de sellado marginal y resistencia adhesiva en resina Bulk ­ Fill aplicando gel de EDTA al 18% en comparación al gel de ácido fosfórico al 37% en el acondicionamiento dental. Materiales y métodos. El tipo de estudio fue transversal, comparativo, de nivel aplicativo y diseño experimental. La muestra estuvo conformada por 60 dientes con cavidades clase I; se realizó el acondicionamiento con gel de ácido fosfórico, gel del EDTA al 18% en 60 segundos y 90 segundos. El total de las muestras fueron incubados a 37°C por 24 horas, se termocicló con 500 ciclos entre 5 a 55ºC. Para evaluar microfiltración, fueron sumergidos en azul de metileno a 37ºC por 4 horas, fueron seccionadas y observados al estereomicroscopio, para realizar la tracción se empleó la máquina de ensayos universales a una velocidad de 0.75mm/min hasta que se desprendiera el tornillo con la resina. Resultados. Las muestras acondicionadas con ácido fosfórico al 37% presenta mayor microfiltración grado 1 y el promedio de su resistencia adhesiva es de 7.97Mpa, la microfiltración obtenida con EDTA en 60 segundos presenta equidad entre grado 1 y 2; promedio de resistencia a la tracción de 8.8 Mpa y el EDTA 90 segundos presentó mayor microfiltración grado 1 y el resto 0 y 2; el promedio de resistencia fue 9.2 Mpa. Conclusión. No existen diferencias estadísticamente significativas al comparar los acondicionantes para la prueba de resistencia adhesiva, sin embargo se observó mejor sellado marginal cuando se acondicionó con gel de EDTA al 18 % por 90 segundos.

Comparación del tiempo de cicatrización entre N-butil cianoacrilato y ácido poliglicólico en caninos sometidos a esterilización / Comparison of healing times between N-butyl cyanoacrylate and polyglycolic acid in canines subjected to sterilization

RESUMEN El objetivo de este estudio fue comparar el tiempo de cicatrización entre N-butil cianocrilato (NBC) y ácido poliglicólico (AC) sobre el cierre tisular en caninos sometidos a operaciones de esterilización. Se realizó un estudio observacional, comparativo y descriptivo sobre una población de 80 perros (Canis familiaris) vivos. Los animales se dividieron en cuatro grupos de 20 perros cada uno según sexo y material de sutura, así: primero grupo, hembras que recibieron NBC; segundo grupo, machos y NBC; tercero grupo, hembras y AC como medio de sutura en piel y cuarto grupo, machos y AC. La técnica quirúrgica en hembras fue oforosalpingohisterectomia y en machos orquiectomia. El tiempo de cierre fue estadísticamente (p < 0,05) menor en los grupos de machos y hembras con el adhesivo NBC comparado con los dos grupos tratados con AC. Se concluye que el NBC es un material seguro y eficaz como medio de fijación tisular en ambas técnicas quirúrgicas que disminuye los días de cierre y recuperación.

ABSTRACT The aim of this study was to compare N-butyl cyanoacrylate (NBC) and polyglycolic acid (AC) in tissue closure in canines subjected to sterilization operations. An observational, comparative and descriptive study was conducted in a population of 80 living dogs (Canis familiaris). The animals were divided into 4 groups of 20 dogs each, according to gender and suture material: the first group consisted of females that received NBC; the second group consisted of males that received NBC; the third group consisted of females that received AC as skin suture; and the fourth group was formed by males that received AC. The surgical technique in females was salpingo-oophorectomy, and in males it was orchiectomy. The closure time was statistically (p < 0.05) lower in the male and female groups with the NBC adhesive in comparison to the two groups treated with AC. It was concluded that NBC is a safe and effective material for tissue fixation in both surgical techniques, decreasing times of closure and recovery.

Influencia del silano y adhesivos universales en la adhesión durante la reparación de un cerómero / Influence of silane and universal adhesives on adhesion during the repair of a ceromer

RESUMEN Introducción: No existe un protocolo definitivo para la reparación de cerómeros. Los adhesivos universales debido a su composición e indicaciones pueden ser una alternativa dentro de la reparación de restauraciones poliméricas, pero la asociación de los silanos con los adhesivos universales requiere más investigación. Objetivo: Evaluar y comparar la resistencia de unión de dos adhesivos universales en la interfase cerómero-resina, asociado o no a un agente silano. Material y métodos: Se realizaron seis bloques de cerómero y se trataron según las siguientes variables: (A) sin tratamiento, (B) agente silano, (C) adhesivo universal 1 + silano, (D) adhesivo universal 1, (E) adhesivo universal 2 + silano, (F) adhesivo universal 2 (n = 10). Se unió resina compuesta a dichas superficies y se realizó prueba de microtensión. El tipo de falla se evaluó con estereomicroscopio. Resultados: Los valores de resistencia de unión de los grupos fueron estadísticamente diferentes (p < 0.05), excepto entre ambos adhesivos universales evaluados. El grupo B presentó los valores más altos de resistencia adhesiva. Los grupos C y E obtuvieron valores de resistencia adhesiva menores en comparación con los grupos D y F. El tipo de falla predominante fue el adhesivo. Conclusión: El uso asociado de un silano funcional con los adhesivos universales no mejora los valores de resistencia adhesiva, por lo que debería evitarse. Como primera elección se recomienda el silano funcional, y en segundo grado, sólo usar adhesivos universales, pero no asociar los dos materiales en un mismo proceso adhesivo.

ABSTRACT Introduction: There is no definitive protocol for ceromer repairs. Universal adhesives due to their composition and indications may be an alternative for polymeric restorations repair. But the association of silanes with universal adhesives requires more research. Objective: To evaluate and compare the bond strength of two universal adhesives in ceromer - resin interface, associated or not with a silane agent. Material and methods: Six ceromer blocks were made and treated according to the following variables: (A) No treatment, (B) Silane agent, (C) Universal Adhesive 1 + Silane, (D) Universal Adhesive 1, (E) Adhesive Universal 2 + Silane, (F) Universal Adhesive 2 (n = 10). Composite resin was attached to these surfaces and a microtension test was performed. The type of failure was evaluated with a stereomicroscope. Results: The bond strength values of the groups were statistically different (p <0.05), except between both universal adhesives were evaluated. Group (B) presented the highest values of adhesive resistance. Groups (C and E) had lower adhesive strength values compared to groups (D and F). The most prevalent type of failure was the adhesive. Conclusion: The associated use of functional silane to universal adhesives does not improve adhesive strength values, so it should be avoided. As a first choice, functionalsilane is recommended, and in the second degree, only use universal adhesives, but do not associate the two materials in the same adhesive process.

Alternativas de tratamientos de superficie para adhesión de cerámica de disilicado de litio / Alternatives of surface treatments for adhesion of lithium disilicate ceramics

Introduction: the clinical success of a restoration is strongly associated with the quality and durability of the ceramic-cement resin interface. In order to obtain an adequate union between these materials of different nature surface treatments are used and achieve mechanical retention or chemical interaction. Objectives: to check if any method promotes a true chemical bond between lithium disilicate ceramics and resin cement. As well as determineif there is any treatment that reports bonding values comparable to hydrofluoric acid and silane (gold standard). Methods: a systematic literature review was developed based on the PRISMA strategy, where the databases were searched: Science Direct, Pubmed (MEDLINE), EMBASE, Springer Journal, SciELO with MeSH and free terms from 2005 to November 2016 for articles in English and Spanish on surface treatments for lithium disilicate. Results: from 58 publications selected a sample of 21 articles. Two articles reported high risk of bias. Conclusions: hydrofluoric acid and silane continue to be the method with the highest and most reliable adhesion values in the literature. Universal adhesives are an alternative to promote chemical adhesion additional to the silane. Diamond burs, Nd: YAG and Er: YAG laser are not recommended as surface treatments(AU)

Introducción: el éxito clínico de una restauración se asocia fuertemente a la calidad y duración de la interface cerámica-cemento resinoso. Para que exista una adecuada unión entre estos materiales de distinta naturaleza se emplean tratamientos de superficie para lograr una buena retención mecánica o interacción química. Objetivos: revisar si algún método promueve una verdadera adhesión química entre la cerámica de disilicato de litio y el cemento resinoso, así como determinar si existe algún tratamiento que reporte valores de unión comparables al ácido fluorhídrico y silano (patrón de oro). Métodos: se desarrolló una revisión sistemática de literatura basada en la estrategia PRISMA, donde se buscó en las bases de datos: Science Direct, Pubmed (MEDLINE), EMBASE, Springer Journal, SciELO con términos MeSH y libres desde el 2005 a noviembre de 2016 para artículos en inglés y español sobre tratamientos de superficie para disilicato de litio. Resultados: de 58 publicaciones, se seleccionó una muestra de 21 artículos. Dos artículos reportaron riesgo de sesgo alto. Conclusiones: el ácido fluorhídrico y silano continúan siendo el método con los valores de adhesión más altos y confiables de la literatura. Los adhesivos universales son una alternativa para promover adhesión química adicional al silano. Fresas diamantadas, laser Nd: YAG y Er:YAG no se recomienda como tratamientos de superficie(AU)

Resistencia al cizallamiento utilizando adhesivo de grabado total y autograbante con y sin hipoclorito de sodio en dentina / Shear strength using total and self etching adhesive with and without sodium hypochlorite in dentin

Es un estudio de investigación cuantitativo donde el objetivo fue determinar la resistencia al cizallamiento utilizando adhesivo de grabado total y autograbante, introduciendo la desproteinización con NaOCl al 5.25 por ciento en dentina y comparar sus valores de resistencia. El estudio se realizó en 31 molares seccionados mesiodistalmente y vestibulo lingual, obteniendo 124 especímenes, se suspendieron en acrílico, pulieron y colocaron en refrigeración a 36 oC durante 48 horas; fueron clasificados en grupos A: Prime & Bond NT, B: NaOCl + Prime & Bond NT, C: NaOCl + Xeno® IV y D: Xeno® IV; se fotoactivó un cilindro de resina compuesta ESTHET-X HD de Dentsply, se mantuvo por 24 horas en horno Felisa con 100 por ciento de humedad, finalmente se probaron en la máquina INSTRON a una velocidad de 1 m/min. Se obtuvieron los siguientes promedios, grupos: A: 6.26, B: 7.71, C: 12.03 y D: 15.06 MPa. Para el grupo C y D que pertenecen al grupo autograbante, fueron estadísticamente significativos para el sustrato dentinal. NaOCl no mostró significancia entre los grupos.

It is a quantitative research where the objective was to determinethe shear strength using total and self etching adhesive, introducing de proteinization with 5.25% NaOCl in dentin and comparing its resistance values. The study was performed on 31 mesiodistally andbuccololingual sectioned molars, obtaining 124 specimens, suspended in acrylic, polished and placed in refrigeration at 36 oC for 48 hours;Were classified into groups A: Prime & Bond NT, B: NaOCl + Prime& Bond NT, C: NaOCl + Xeno® IV and D: Xeno® IV; A: DentsplyESTHET-X HD composite resin cylinder was photoactivated, kept for24 hours in a Felisa oven with 100% humidity, finally tested on theINSTRON machine at a speed of 1 mm/min. The following averageswere obtained, groups: A: 6.26, B: 7.71, C: 12.03 and D: 15.06 MPa.For group C and D belonging to the self-etching group, they werestatistically significant for the dentinal substrate. NaOCl, showed nosignificance between the groups.

Adhesión después del uso de dentífricos: Una revisión de la literatura / Bonding after the use of toothpastes: A literature review

La adhesión representa uno de los procedimientos de mayor empleo en la odontología restauradora, para ello el sistema adhesivo debe contar con propiedades mecánicas ideales, pues su técnica es muy sensible. Muchos reportes indican que el uso de dentífricos puede afectar el proceso de adhesión al sustrato dental, sea esmalte o dentina, y puede variar de acuerdo a su composición. Algunos pueden afectar obliterando los túbulos dentinarios, así también las pastas blanqueadoras liberan radicales libres por un tiempo determinado y pueden afectar la fotopolimerización del material. En la literatura existe controversia del efecto de estos productos sobre la adhesión, es por eso que el objetivo de la presente revisión es mostrar la evidencia científica del efecto de los dentífricos con diferentes principios activos en la resistencia de los sistemas adhesivos a la estructura dental.

Bonding represents one of the largest employment procedures in restorative dentistry, for which the adhesive system should have ideal mechanical properties because their technique is very sensitive. Many reports indicate that the use of toothpaste can affect the process of bonding of the dental substrate, either enamel or dentin, and may vary according to its composition. Some may affect obliterating the dentinal tubules, so whitening toothpaste free radicals released by a certain time and can affect the ligthtcuring of the material. There is controversy in the literature about the effect of these products on bonding, the purpose of this review is to show the scientific evidence of the effect of toothpastes with different active principles in the strength of bonding systems to the dental structure.

In vitro evaluation of bond strength of four self-etching cements

Indirect restorations need to be attached with adhesive luting agents to prevent them from becoming dislodged and provide adequate marginal sealing. The aim of this study was to evaluate bond strength to dentin of selfetching resin cements. Materials and methods: 75 flat dentin surfaces were randomly distributed among 5 groups, according to cements used; Group 1: RelyxU100 (3M/ESPE), Group 2: Bis Cem (Bisco), Group 3: Max Cem (Kerr), Group 4: SeT PP (SDI) and Group 5: Relyx ARC (3M/ESPE), control. Ceramic test cylinders (IPS Empress 2 / IvoclarVivadent) 4.1 mm across were prepared and attached to the dentin surfaces using the different cements. A constant 25N load was applied for 1 minute and they were lightpolymerized. Following storage for 24 hours at 100% humidity and 37 °C, the specimens were tested for bond strength under shear strain in an Instron testing machine at a crosshead speed of 1 mm/minute; at 7, 14 and 21 days. Data were analyzed by ANOVA and Tukey's test. There were significant differences between materials (p < 0.0001), but not between times or material/time interaction. RelyX ARC (Control Group) had the highest bond strength (15.52 MPa). Among the selfetching cements, the best behavior was found for Relyx U100 (10.80MPa), followed by BisCem (6.36 MPa), MaxCem (5.45 MPa) and SeTPP (3.17 MPa). The bond strength of the selfadhesive cements evaluated was lower than that for resin cements which require previous treatment of the dental substrate (control group). This should be taken into account during clinical selection, in particular for tooth preparations with poor retention (AU)

Las restauraciones indirectas deben ser fijadas por medio de agentes cementantes, para evitar su desprendimiento y mantener un adecuado sellado marginal. El objetivo de este trabajo fue evaluar la resistencia adhesiva a dentina de los cementos resinosos de autograbado. Materiales y métodos: Se utilizaron 75 superficies planas de dentina, distribuidos aleatoriamente en 5 grupos, según los medios cementantes; GRUPO 1: RelyxU100 (3M/ESPE), GRUPO 2: Bis Cem (Bisco), GRUPO 3: Max Cem (Kerr), GRUPO 4: SeT PP (SDI) y GRUPO 5: Relyx ARC (3M/ESPE), control. Se confeccionaros probetas cilíndricas de cerámica (IPS Empress 2 / IvoclarVivadent) de 4,1 mm de diámetro, las que fueron fijadas a las superficies de dentina mediante los distintos cementos. Se aplicó una carga constante de 25N durante 1 minuto y se realizó la fotopolimerización. Después de 24 horas de almacenamiento en un medio con 100 % de humedad a 37° C, las probetas fueron sometidas a ensayo de resistencia adhesiva bajo tensiones de corte en máquina Instron, con una velocidad del cabezal de 1 mm/minuto; a los 7, 14 y 21 días. Los datos fueron analizados mediante ANOVA y test de Tukey, mostrando diferencias significativas entre los materiales (p < 0,0001), no así respecto al factor tiempo ni a su interacción. El mayor valor de resistencia adhesiva lo presentó RelyX ARC (Grupo control) (15,52MPa), De los cementos autograbantes, el mejor compor ta miento se obtuvo en Relyx U100 (10,80MPa), seguido por BisCem (6,36MPa), MaxCem (5,45MPa) y SeTPP (3,17MPa): Los cementos autoadhesivos evaluados presentaron menor resistencia adhesiva que los cementos resinosos que requieren tratamiento previo del sustrato dentario (grupo control). Esto debería ser considerado cuando se realiza su selección clínica, sobre todo en preparaciones dentarias poco retentivas (AU)

Efecto de los diferentes tiempos de grabado ácido sobre la resistencia de unión de un sistema adhesivo autoacondicionante en esmalte bovino / Effect of the different acid etching times over the bond strenght of a self etching adhesive system in bovine enamel

OBJETIVO: Comparar el efecto de los diferentes tiempos de grabado ácido (0, 10, 20 y 30 segundos) sobre la resistencia unión de un sistema adhesivo autoacondicionante en esmalte bovino. MATERIALES Y MÉTODO: Este estudio fue experimental, in vitro. Se utilizaron 8 dientes bovinos, distribuidos aleatoria-mente, de los cuales se obtuvieron 120 especímenes; que fueron divididos en 4 grupos (n=30); según los diferentes tiempos de grabado ácido al 37 % (Scotchbond-3M Espe); un grupo control (G1: sin grabado ácido.) y tres grupos experimentales (G2: 10, G3: 20 y G4: 30 segundos) haciendo uso de un sistema adhesivo autoacondicionante (All-Bond Universal. Bisco). Se aplicó la prueba de microtensión a todos los especímenes obtenidos a una velocidad de 1.0 mm/min. Se realizó un análisis univariado, luego un análisis bivariado ANOVA One-Way, y por último la prueba Post Hoc de HSD de Tukey. El intervalo de confianza fue de 95 % y el criterio de significancia p< 0.05.RESULTADOS: Los promedios de la resistencia de unión de los 4 grupos de diferentes tiempos de grabado ácido fueron: Grupo 1: 16.81 MPa (DE ± 4.95), Grupo 2: 26.23 MPa (DE ± 5.60), Grupo 3: 25.29 MPa (DE ± 7.43) y Grupo 4: 20.19 MPa (DE ± 3.55), se encontró entre estos promedios diferencias estadísticamente significativas p<0.001. Se hicieron comparaciones por grupos usando el análisis bivariado ANOVA One-Way y Post Hoc de HSD de Tukey, con los siguientes resultados: Al comparar los grupos 1 y 2 (0 seg. ­ 10 seg.); el valor p=0.000, el grupo 1 y 3 (0 seg. - 20 seg.); el valor p=0.000 y los grupos 2 y 4 (10 seg. ­ 30 seg. ); el valor p=0.000. CONCLUSIÓN: Existen diferencias estadísticamente significativas al comparar los diferentes tiempos de grabado ácido (grupo control y los 3 grupos experimentales) sobre la resistencia de unión de un sistema adhesivo autoacondicionante en esmalte bovino. El Grupo 2 presentó una mayor resistencia de unión. (AU)

OBJECTIVE: To compare the effect of different acid etching times (0, 10, 20 and 30 seconds) on the bond strength of a self-etching adhesive system in bovine enamel. MATERIALS AND METHODS: This study was experimental, in-vitro. Eight bovine teeth were used, randomized, of which 120 specimens were obtained; they were divided into 4 groups (n=30); according to the different acid etching times at 37 % (Scotch-bond-3M Espe); control group (G1: without acid etching) and three experimental groups (G2:10, G3: 20 and G4: 30 seconds) using a self-etching adhesive system (All-Bond Universal. Bisco). A microtensile test was applied to all the specimens obtained at a speed of 1.0 mm/min. Univariate analysis was performed, then a bivariate analysis One-Way ANOVA and finally Tukey ́s HSD Post Hoc test. The confidence interval was 95% and the significance criteria was p<0,05.RESULTS: The average of bond strength of the 4 groups of different acid etching times evaluated were: Group 1: 16.81 MPa (SD ± 4.95), Group 2: 26.23 MPa (SD ± 5.60), Group 3: 25.29 MPa (SD ± 7.43) and Group 4: 20.19 MPa (SD ± 3.55). It was found among these averages statistically significant differences p<0.001. Comparisons were made by groups using bivariate analysis One-Way ANOVA and Tukey's HSD Post-Hoc, with the following results: When comparing groups 1 and 2 (0 sec.- 10 sec); p-value=0.000, groups 1 and 3 (0 sec. - 20 sec); p-value=0.000 and groups 2 and 4 (10 sec. - 30 sec.); p-value=0.000.CONCLUSION: There were statistically significant differences when comparing different acid etching times (control group and the three experimental groups) on the bond strength of a self-etching adhesive system in bovine enamel. Group 2 had a higher bond strength. (AU)